  • Creep-fatigue crack growth behavior was experimentally measured particularly when a crack was located in the heat affected region of 1Cr-0.5Mo steel. Load hold times of the tests for trapezoidal fatigue waveshapes were varied among 0, 30, 300 and 3,600 seconds. Time-dependent crack growth rates were characterized by the <TEX>$$C_t$$</TEX>parameter. It was found that the crack growth rates were the highest when the crack path was located along the fine-grained heat affected zone(FGHAZ). Cracks located in other heat affected regions had a tendency to change the crack path eventually to FGHAZ. Creep-fatigue crack growth law of the studied case is suggested in terms of (da/dt<TEX>$$)_{avg}$$</TEX> vs. (<TEX>$$C_t$$</TEX><TEX>$$)_{avg}$$</TEX> for residual life assessment. (rdf:langString) (en)
nlon:biographicalNote
  • 백운봉, 회원, 한국표준과학연구원 산업측정표준부, ubbaek (rdf:langString) (kriss.re.kr)
  • 서창민, 회원, 경북대학교 기계공학부 (xsd:string)
  • 윤기봉, 회원, 중앙대학교 기계공학부 (xsd:string)
  • 이해무, 회원, 한국표준과학연구원 산업측정표준부 (xsd:string)
nlon:classificationNumberOfNLK
  • 550.5 (xsd:string)
nlon:containedIn
dc:creator
  • 백운봉 (xsd:string)
  • 서창민 (xsd:string)
  • 윤기봉 (xsd:string)
  • 이해무 (xsd:string)
dcterms:creator
nlon:datePublished
  • 2021-01-30T23:37:12 (xsd:dateTime)
dcterms:description
  • Creep-fatigue crack growth at CrMo steel weld interface (xsd:string)
bibframe:extent
  • 26 cm (xsd:string)
  • p. 3088-3095 (xsd:string)
dcterms:isPartOf
nlon:issuedYear
  • 2000 (xsd:string)
nlon:itemNumberOfNLK
  • 대446 (xsd:string)
rdfs:label
  • CrMo강 용접계면균열의 크리프-피로 균열성장거동 / 백운봉, 윤기봉,이해무,서창민 (xsd:string)
dcterms:language
dc:subject
  • C* (xsd:string)
  • Creep-fatigue crack growth (xsd:string)
  • Ct (xsd:string)
  • HAZ (xsd:string)
  • Life assessment (xsd:string)
  • Weld interface (xsd:string)
  • 수명평가 (xsd:string)
  • 열영향부 (xsd:string)
  • 용접계면 (xsd:string)
  • 크리프-피로 균열성장 (xsd:string)
dcterms:title
  • CrMo강 용접계면균열의 크리프-피로 균열성장거동 (xsd:string)
rdf:type
nlon:volumeOfNLK
  • 24(12) (xsd:string)